Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.
Did not do the adhesion test of powder spraying or fluorocarbon spray on the packaging galvanized wire, but there are two points for reference: one, in the sealed or air circulation environment, non-metallic volatiles can corrosion zinc coating; Second, zinc above 230 degrees (c) will brittle the base metal. After powder spraying and fluorocarbon spraying, it is necessary to bake at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in decreased adhesion of coating, and even leading to brittle situation of steel wire.
Because the bundled galvanized wire is endowed with pre-tension, so it has the excellent characteristics of low relaxation value, small stress loss, good stability after loading, not easy to deformation, no fracture, strong elasticity, ordinary steel lines and rebar is difficult to match. The use of advanced galvanized finishing process, therefore, the use of hot-dip galvanized steel wire construction, not only good anti-corrosion performance, and beautiful generous. The product has the characteristics of smooth surface, high dimensional precision, good uniformity of zinc layer and firm adhesion.
Post time: 28-10-22