Hot plating wire can generate thicker coating, and there are both pure zinc layer and iron zinc alloy layer, so the corrosion resistance is better. The production power of hot dip galvanizing is particularly high, and the duration of the parts in the hot dip galvanizing tank usually does not exceed lmin. Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. To plate, tape, wire, tube and other profiles plating, automation degree is higher.
“Wet” hot dip galvanizing is also called “molten solvent method” hot dip galvanizing. Iron and steel workpiece through degreasing, pickling and cleaning, it is necessary to set in a special box above the surface of the molten zinc in the “molten solvent” (also called cosolvent), and then into the zinc liquid to galvanized. The molten solvent is usually a mixture of ammonium chloride and zinc chloride, but also other chlorine salts.
“Dry” hot dip galvanizing is also called “drying solvent method” hot dip galvanizing. Iron and steel work pieces through degreasing, pickling, cleaning, dipping aid solvent and drying, and then immersed in the molten zinc solution to galvanize. The co-solvent is usually hydrochloric acid, ammonium chloride, or ammonium chloride mixed with zinc chloride in aqueous solution.
Scope of use: Because the obtained coating is thicker, hot-dip galvanizing has very good protective function than electric galvanizing, so it is an important maintenance coating for iron and steel parts in strict working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding and other occupations. In agriculture, such as pesticide irrigation, greenhouse and construction industry, such as water and gas transportation, wire casing, scaffolding, Bridges, highway guardrail and other aspects, have been widely used in these years.
Post time: 17-02-23